Delivery forms
Ingots with and without suspension
Rods Typ 3K (triangular) & 4K (quadrangular)
Massive solder and flux cored solder wires
Pellets (hemisphere sections)
Sticks® (Cylinders)
Other formats or products not listed here may be possible after consultation.
Applications
• High Temperature Solder
• Tinning of enamelled Copper Wires up to about 570 °C
• Transformers Manufacture
• Dip Tinning
• Electronics Manufacturing
• Electrical Works
Products
Sticks made from Pb93,5Sn5Ag1,5
1201
molded
none
without
triangular
Sticks
400 mm
10 mm
10 mm
1200
molded
none
without
square cut
Sticks
340 mm
30 mm
20 mm
The products shown are only a selection from our product range. Please contact us for your desired configuration of Sticks from Pb93,5Sn5Ag1,5.
Material properties
| Melting temperature °C | 296-301 |
| Solder wave temperature °C | k.A. |
| Density g/cm³ | ~11,02 |
| Hardness HB | k.A. |
| Tensile strength N/mm² | k.A. |
| Stretching % | k.A. |
| Specific heat of fusion J/g | k.A. |
| Electrical conductivity µΩcm | k.A. |
This alloy can be stored for at least 48 months if properly stored in a clean and dry environment. For massive formats, further processing is usually possible after the specified storage period has expired, but should be technically checked and approved in advance.
Chemical composition in accordance with the factory standard
(Data in percent by weight)
| Element | Formular | Composition |
|---|---|---|
| Lead | Pb | Residue |
| Tin | Sn | 4.8-5.2 |
| Silver | Ag | 1.2-1.8 |
| Antimony | Sb | < 0.2 |
| Bismuth | Bi | < 0.1 |
| Indium | In | < 0.1 |
| Copper | Cu | < 0.08 |
| Gold | Au | < 0.05 |
| Arsenic | As | < 0.03 |
| Iron | Fe | < 0.02 |
| Nickel | Ni | < 0.01 |
| Cadmium | Cd | < 0.002 |
| Aluminium | Al | < 0.001 |
| Zinc | Zn | < 0.001 |
The data shown in the table is based on our internal material specification.
Get your offer
Fast, transparent and uncomplicated - request your individual offer now!
Your contact person
Maxim Richter
Head of Sales & Logistics